Flange IX Seal Rings
Many clients have drawn on SUNWELL`s specialized knowledge and experience on the use of high pressure and high temperature metal-to-metal static sealing. SUNWELL have developed a sealing system which uses a modified cone ring giving excellent leak tightness properties under the most severe conditions of pressure, temperature, thermal cycling and shock.
IX Seal Rings are designed and used where NORSOK CFC (Compact Flange Connections) are in use.
The rings come in three different kinds of steel and are coated with PTFE in varying colors in order to distinguish between them
(Standard identification NORSOK)
The designed or materials shall be selected, so that main sealing ares can not be subject to corrosion.
Typical Seal Ring Materials:
Typical minimum yield stress and ultimate stress of the seal ring material shall at maximum design temperature be 300MPa and 360MPa, respectively, in order to allow for reasonably elastic spring-back.
Lower strength may be used, but is not recommended.
The user is responsible for selecting a seal ring material which is suitable for the service medium and the design temperature conditions.
Seal ring materials are commonly chosen to be compatible with the flange material,
I.e. Duplex seal ring in duplex flange.
IX Seal Ring Selection: | Flange Material | Service Temp. | Seal Ring Material | Seal Ring PTFE Color | | Carbon Steel | -50oC to +250oC | CS,316L,Low Alloy Steel (AISI4140) | Blue | | Stainless Steel | -50oC to +250oC | 22Cr Duplex | Yellow | | Stainless Steel | -50oC to +250oC | 17/4-PH | Orange | | Stainless Steel | -101oC to +250oC | Nickel Alloys (Inconel 625 etc) | Black | \ n \ nCoating: \ nLes anneaux d'étanchéité doivent être enduits d'un revêtement PTFE de 10μm à 30μm & période; La couleur du revêtement doit être conforme à l'exigence ci-dessus tableau & période; \ n \ nSurface Finition: \ nToutes les surfaces des anneaux de mer doivent être usinées avec une rugosité de surface maximale conformément au tableau ci-dessous: | Location | Ra max μm | | Sealing Faces | 0,8 | | All other Surfaces | 6,3 | Les efforts axiaux de la bague IX Seal Ring sont exercés sur le cône de la bague d'étanchéité métallique et se traduisent par une force d'étanchéité radiale & period; De plus, avec une précharge accrue, le biseau est fermé et le contact face à face est réalisé au coin externe tandis que la plus grande partie de la précharge du boulon est transférée comme forces de compression entre les faces de la bride au niveau du talon. joints et période; Le premier joint est créé par l'application de la contrainte d'assise du joint sur le talon et la période de la bride; La bride reste également en contact le long de la circonférence extérieure de la tombe sur les faces de la bride pour tous les niveaux de charge admissibles. Le sceau principal est l'anneau et la période d'étanchéité IX; La force de la bague d'étanchéité est fournie par l'énergie élastique stockée dans la bague d'étanchéité et la période de contrainte; Toute fuite de l'enfer donnera une pression interne agissant sur l'anneau d'étanchéité à l'intérieur de l'intensification de l'action d'étanchéité & période; \ nLa conception vise à prévenir l'exposition à l'oxygène et d'autres agents corrosifs & période; Ainsi, cela empêche la corrosion des faces de la bride, la longueur sous tension des boulons et la bague d'étanchéité et la période; \ n \ nIsolation de la bague d'étanchéité: \ n \ nTaille et poids: \ nLes anneaux IX n'ont qu'une seule dimension par DN & lpar; Diamètre nominal & rpar; qui couvre toutes les classes de pression | DN | NPS | IX Dimension | Weight (kg) | | 15 | 1/2" | IX15 | 0,02 | | 20 | 3/4" | IX20 | 0,03 | | 25 | 1" | IX25 | 0,03 | | 40 | 1 1/2" | IX40 | 0,05 | | 50 | 2" | IX50 | 0,08 | | 65 | 2 1/2" | IX65 | 0,12 | | 80 | 3" | IX80 | 0,17 | | 100 | 4" | IX100 | 0,28 | | 125 | 5" | IX125 | 0,42 | | 150 | 6" | IX150 | 0,62 | | 200 | 8" | IX200 | 0,99 | | 250 | 10" | IX250 | 1,85 | | 300 | 12" | IX300 | 2,18 | | 350 | 14" | IX350 | 2,60 | | 400 | 16" | IX400 | 3,43 | | 450 | 18" | IX450 | 4,38 | | 500 | 20" | IX500 | 5,27 | | 550 | 22" | IX550 | 6,48 | | 600 | 24" | IX600 | 7,55 | | 650 | 26" | IX650 | 8,74 | | 700 | 28" | IX700 | 10,40 | | 750 | 30" | IX750 | 11,80 | | 800 | 32" | IX800 | 13,30 | | 850 | 34" | IX850 | 14,80 | | 900 | 36" | IX900 | 17,10 | | 950 | 38" | IX950 | 18,90 | | 1000 | 40" | IX1000 | 20,90 | | 1050 | 42" | IX1050 | 23,00 | | 1100 | 44" | IX1100 | 25,10 | | 1150 | 46" | IX1150 | 27,50 | | 1200 | 48" | IX1200 | 29,90 | Caractéristiques: \ n> Formats de taille 10mm à 1700mm actuellement en service & semi; \ n> Plus la pression est élevée, plus la conception SUNWELL devient attrayante car la pression interne intensifie l'action d'étanchéité et la bague d'étanchéité peut être à haute température. La température de service maximum étant limitée par le matériau de joint sélectionné & period; Matériaux allant du carbone et de l'acier allié à l'inconel, avec une gamme de revêtement pour la lubrification & semi; \ n> Le système d'étanchéité est extrêmement étanche dans les conditions les plus sévères de pression, température, vide, et convient aux applications nucléaires & semi; > Les conditions de trempe froide et de cyclage thermique sont la cause de la plupart des problèmes de fuite lorsque des joints de type compressible conventionnels et des matériaux d'étanchéité sont utilisés & period; La flexibilité supplémentaire de la bague d'étanchéité IX assure une étanchéité parfaite en conditions transitoires thermiques. Des conceptions de bride compactes et plus légères peuvent généralement être obtenues en utilisant des bagues d'étanchéité IX & period; Les joints d'étanchéité et les articulations sont plus bas que les joints de type compressible conventionnels. La bague d'étanchéité tout IX est de conception élastique et lors du démontage revient à sa forme d'origine prête à être réutilisée & period; Tous les joints d'une taille donnée sont interchangeables sans aucun pré-ajustement & période; Groupes de Produits : Joints d'étanchéité
|